Method for preparing homo-and co-polymers of cyclic olefin compounds

ABSTRACT

The present invention relates to a method for preparing homo- and co-polymers having high molecular weights in high yields by polymerizing cyclic olefin compounds using a complex prepared by mixing a nickel salt compound, an organoaluminoxane compound, and at least one fluorine-containing compound.

BACKGROUND OF THE INVENTION

1. The Field of the Invention

This invention relates to a method for preparing homo- and co-polymers of cyclic olefin compounds. More particularly, this invention relates to a method for preparing homo- and co-polymers by polymerization of cyclic olefin compounds that uses a fluorine-containing compound as a catalyst activator, forming a homogeneous catalyst system having a high solubility in a non-polar solvent, together with a nickel salt compound and an organoaluminoxane compound to prepare cyclic polymers having high molecular weights in high yields.

2. Related Prior Art

The copolymer of a cyclic olefin compound and ethylene or propylene is endowed with excellent properties such as transparency, heat resistance, etc., which hardly appear in the existing polymers such as polyethylene or polypropylene, with the introduction of a rigid ring structure such as norbornene into the main chain of the polymer. Accordingly, the homopolymer/copolymer of a cyclic olefin compound is expected to substitute for a polycarbonate (PC) or polymethylmethacrylate (PMMA) resin currently used as an information recording material, and possibly utilized as an optical material with transparency and low moisture absorption for various applications such as DVD, CD, lens, optical fiber, and the like.

Currently, various norbornene derivatives having different alkyl groups and polar functional groups are used for the preparation of cyclic olefin polymers. Such norbornene derivatives are useful for the preparation of homopolymers as well as copolymers using ethylene or propylene.

Some advanced manufacturers of cyclic olefin polymers have recently been developing novel materials having epoch-making thermal, mechanical and optical properties, which are unattainable by the existing polyolefins, through copolymerization of styrene, cyclic olefin, methylmethacrylate, or the like. In particular, the polymers prepared by copolymerization of cyclic olefin and ethylene are standing in the spotlight as a next-generation information recording material such as CD, DVD, and so forth due to their remarkably excellent optical and thermal properties.

The norbornene polymers not only substitute for polycarbonate used for the aforementioned applications but also reduce the space between CD tracks to allow high integration, so they are applicable to next-generation DVD (e.g., HD-DVD), or the like. In addition, such norbornene polymers are widely used for more various applications such as camcorders or automobile cameras due to their excellent properties such as optical properties, dimensional stability, excess moisture tolerance, low density, and so forth.

The polymerization catalysts for preparation of a polymer using a cyclic olefin compound can be classified into an addition polymerization catalyst, a ROMP (Ring Opening Metathesis Polymerization) catalyst, and a cationic catalyst, including a radical initiator.

Among these, the addition polymerization catalyst, the ROMP catalyst and the cationic catalyst have a common characteristic that they can be used for preparation of cyclic olefin polymers with high transparency. The use of the ROMP catalyst necessarily demands a step of saturating the double bonds of the polymer after polymerization, and the addition polymerization catalyst is used for preparation of a cyclic olefin polymer having a low dielectric property (i.e., insulating property).

The representative metals constituting the addition polymerization catalyst include Ti, Zr, Cr, Co, Ni, Pd, and the like. Among these metals, Ni and Pd are representative metals for preparation of a cyclic olefin polymer.

The representative main metals constituting the ROMP catalyst include Mo. W, Ru, Re, or the like. The activity of the catalyst can be controlled through a modification of the ligands around the metal or a change in the additives.

The cyclic olefin polymer, whose principal advantages are low density, high transparency, low moisture absorbency, and heat resistance, is expected to substitute for glass, acrylic polymer, polycarbonate, and polyvinylidene chloride (PVDC).

As an example of the conventional methods using a transition metal as a polymerization catalyst in the preparation of homo- and co-polymers from norbornene and its derivatives, U.S. Pat. No. 3,330,815 discloses a method for addition polymerization of norbornene using a complex prepared from TiCl₃ (or TiCl₄) and an organoaluminum compound, or Pd(C₆H₅CN)₂Cl₂ as a catalyst. Disadvantageously, this method provides a polymer having a number average molecular weight (M_(n)) of less than 10,000 in a low yield.

Another example is a method for addition polymerization of norbornene and its derivatives using a complex prepared by mixing Ni(O) salt, a bidentate ligand, and B(C₆F₅)₃ as disclosed in U.S. Pat. Nos. 6,350,837B1 and 6,538,085B2. In this case, however, one of the components consisting the catalyst, B(C₆F₅)₃, is a very expensive compound, so the method is limited in its industrial uses.

U.S. Pat. No. 5,705,503 discloses a method for addition polymerization of a norbornene derivative using a Zwitterion complex prepared from palladium metal. However, this method requires an excess amount of the catalyst with respect to the amount of the monomer (the molar ratio of monomer to catalyst is less than 250) and a polymerization time of 12 hours or more for a relatively high yield. A similar method is disclosed in U.S. Pat. Nos. 6,262,194B1 and 6,265,506B1, which relates to a method for addition polymerization of norbornene using a Zwitterion complex prepared from palladium metal. This method is also disadvantageous in that the complex should be prepared by coordination of ligands of a specific structure with palladium metal, which makes it difficult to apply the method to industrial large-scaled production of the polymer.

European Patent Application No. 0 504 418A1 (filed on Sep. 23, 1992) discloses a method for addition polymerization of a cyclic olefin compound in the presence of A) a transition metal salt compound, B) a compound capable of forming an ionic complex with the compound A), and C) an organoaluminum compound.

Other examples of the cyclic olefin polymerization method using a transition metal as a catalyst include a cyclic olefin polymerization method using a Zirconocene compound and an aluminoxane compound (Japanese Patent Application Laid-open Kokai No. Sho 64-66216), and a method for copolymerization of norbornene and an olefin compound using a transition metal salt compound and an aluminoxane compound (Japanese Patent Laid-open Nos. 61-221206 and 64-106). However, these methods require an excess amount of the aluminoxane compound, causing discoloration of the product, and requiring a step of removing catalyst residues in the polymer after the polymerization reaction, thus reducing productivity.

Japanese Patent Laid Open Nos. 61-271308 and 62-252406 disclose methods for copolymerization of norbornene and olefin using a catalyst system comprising a vanadium compound and an organoaluminum compound, which methods involve an extremely low catalyst activity.

The methods for addition polymerization of a cyclic olefin compound using a metallocene catalyst are disclosed in U.S. Pat. Nos. 5,087,677 and 5,371,158, which are directed to a method for homo- and co-polymerizations of norbornene derivatives using a Ti-, Zr-, Hf-, V-, Nb- or Ta-based metallocene complex as a main catalyst and an aluminoxane compound as a cocatalyst. However, these methods mostly provide a low polymerization yield of less than 50%.

In addition, U.S. Pat. No. 5,621,054 discloses a method for copolymerization of norbornene and ethylene using a catalyst activator, N,N-dimethylanilinium tetrakis-perfluorophenylboron and a metallocene catalyst prepared by coordinating ligands of a unique structure to a metal such as Hf or Zr without an organoaluminum or aluminoxane compound. Disadvantageously, the method also has the difficulty in application to commercialized processes because of the extremely unique structures of the ligands and the catalyst activator.

In addition to the aforementioned problems, the above-described conventional techniques have the difficulty in forming a homogeneous catalyst system having a high solubility in a non-polar solvent and in preparing a cyclic olefin polymer having a high molecular weight in a high yield.

Compared with a solution polymerization using a homogeneous catalyst system having a high solubility in a non-polar solvent, a solution polymerization using a heterogeneous catalyst system forming a suspended solid due to incomplete dissolution in a non-polar solvent is ready to cause gel formation, so the gel thus produced greatly increases the solution viscosity of the polymer due to the resultant gel and accumulates on the wall of the reactor or the pipe line to inhibit the flow of reactants or products.

Namely, the heterogeneous catalyst system with poor solubility has a difficulty in quantitative control of the catalyst essential to the uniform progress of the reaction and the property control of the product, relative to the homogeneous catalyst system excellent in solubility.

SUMMARY OF THE INVENTION

In an attempt to improve the problems with the prior art, the inventors of the present invention have found out that the use of a mixture of a nickel salt compound, an organoaluminoxane compound and a fluorine-containing compound as a catalyst system provides a method for a preparation of a cyclic polymer having a high molecular weight in a high yield, thus accomplishing the present invention.

It is therefore an object of the present invention to provide a method for preparing a cyclic polymer having a high molecular weight in a high yield by using a homogeneous catalyst system having a high solubility in a non-polar solvent, allowing a simple quantitative measurement of the catalyst and inhibiting gel formation.

To achieve the object of the present invention, there is provided a method for preparing a cyclic polymer having a high molecular weight in a high yield using a complex prepared by mixing a nickel salt compound, an organoaluminoxane compound, and at least one fluorine-containing compound selected from compounds represented by the following formulas 1 to 7: BF₃.OR₁R₂  Formula 1

Wherein, R₁ and R₂ are different or the same and independently include a substituent selected from a C₁–C₁₀ alkyl group, a C₁–C₁₀ cycloalkyl group, a C₁–C₁₀ allyl group, a C₁–C₁₀ aryl group, or C₁–C₁₀ arylalkyl group,

Wherein, R₃ is an alkyl group containing from 2 to 10 carbon atoms. HF.OR₄R₅  Formula 3

Wherein, R₄ and R₅ are different or the same and independently include a substituent selected from a C₁–C₁₀ alkyl group, a C₁–C₁₀ cycloalkyl group, a C₁–C₁₀ allyl group, a C₁–C₁₀ aryl group, or C₁–C₁₀ arylalkyl group,

Wherein, R₆ is an alkyl group containing from 2 to 10 carbon atoms.

-   -   wherein, R₇, R₈ and R₉ are different or the same and         independently include a C₁–C₁₀ alkyl group, a C₁–C₁₀ cycloalkyl         group, a C₁–C₁₀ aryl group, a C₁–C₁₀ arylalkyl group, or a         hydrogen atom,         BF₃ .nR₁₀  Formula 6

Wherein, R₁₀ is H₂O or CH₃COOH; and n is 1 or 2, HF.R₁₁  Formula 7

Wherein, R₁₁ is pyridine.

Hereinafter, the present invention will be described in further detail as follows.

The present invention is directed to a novel method for preparing a cyclic polymer having a high molecular weight in a high yield using a complex prepared by mixing at least one fluorine-containing compound selected from the compounds represented by the formulas 1 to 7 with a nickel salt compound and an organoaluminoxane compound.

The term “cyclic olefin compound” as used herein refers to, if not specifically limited to, at least one selected from norbornene, dicyclopentadiene, and compounds represented by the following formulas 8 and 9, which can be used alone or in combination with at least two of them:

-   -   wherein, R₁₂ is a C₁–C₂₀ alkyl group,     -   wherein R₁₃ is a C₁–C₂₀ alkyl group.

In the addition polymerization of a cyclic compound, the catalyst used herein comprises a nickel salt compound, a fluorine-containing compound, and an organoaluminoxane compound. First, the nickel salt compound is preferably a nickel-carboxylate compound containing ligands of a high solubility in a non-polar solvent. The specific examples of the nickel salt compound may include a nickel salt compound comprising a carboxylate containing at least 6 carbon atoms, such as nickel(hexanoate)₂, nickel(heptanoate)₂, nickel(octanoate)₂, nickel(2-ethylhexanoate)₂, nickel(naphthenate)₂, nickel(stearate)₂, and nickel(versatate)₂. Preferably, the nickel salt compound is used in an amount of 1×10⁻⁵ to 1×10⁻³ mole per 10 g of the monomer.

The specific examples of the fluorine-containing compound may include a boron trifluoride complex represented by the formulas 1 and 2, such as boron trifuloride dimethyl etherate, boron trifluoride diethyl etherate, boron trifluoride dibutyl etherate, and boron trifluoride-tetrahydrofuran complex, etc.; a hydrogen fluoride complex represented by the formulas 3 and 4, such as hydrogen fluoride dimethyl etherate, hydrogen fluoride diethyl etherate, hydrogen fluoride dibutyl etherate, and hydrogen fluoride-tetrahydrofuran complex; a boron trifluoride complex represented by the formula 5, such as boron trifluoride-methylamine complex, boron trifluoride-ethylamine complex, boron trifluoride-propylamine complex, and boron trifluoride-butylamine complex; a boron trifluoride complex represented by the formula 6, such as boron trifuloride dihydrate and boron trifluoride-acetic acid complex; a hydrogen fluoride complex represented by the formula 7, such as hydrogen fluoride-pyridine, etc.

The specific examples of the organoaluminoxane compound may include methylaluminoxane, ethylaluminoxane, propylaluminoxane, butylaluminoxane, isobutylaluminoxane, etc. The use of an alkylaluminum compound that is used as a constituent component for the polymerization of a conventional diene compound, instead of the organoaluminoxane compound, results in an extremely low yield, brining disadvantage in the aspect of economy in the industrial production, and causes a limitation in increasing the molecular weight of the polymer above a predetermined level.

The addition polymerization catalyst for preparation of a cyclic polymer is prepared by mixing the nickel salt compound, the organoaluminoxane compound, and the fluorine-containing compound. The solvent used for preparation of the catalyst is suitably a non-polar solvent inert to the catalyst and specifically includes cyclohexane, hexane, benzene, toluene, chlorobenzene, o-dichlorobenzene, etc.

The fluorine-containing compound represented by the formulas 1 to 7 is mixed with the nickel salt compound at a molar ratio of 1:1 to 30:1, preferably 3:1 to 10:1. The molar ratio of the fluorine-containing compound to the nickel salt compound being less than 1 deteriorates the polymerization yield, while the molar ratio exceeding 30 causes discoloration of the product and deteriorates economical efficiency.

The organoaluminoxane compound and the nickel salt compound are mixed at a molar ratio of 8:1 to 200:1, preferably 15:1 to 100:1. The molar ratio of the organoaluminoxane compound to the nickel salt compound being less than 8 deteriorates the polymerization yield, while the molar ratio exceeding 200 causes a discoloration of the product and a deterioration of the economical efficiency.

The addition sequence of the respective constituent components of the catalyst is in the order of a solution of a nickel salt compound, an organoaluminoxane compound, and then a fluorine-containing compound selected from the compounds of the formulas 1 to 7. This addition sequence can be changed under circumstances.

The catalyst thus prepared is used for addition polymerization of a cyclic olefin to prepare the cyclic polymer of the present invention. The specific examples of the non-polar solvent used for polymerization may include aliphatic hydrocarbons such as hexane, isopentane, heptane, octane, and isooctane; cycloaliphatic hydrocarbons such as cyclopentane, methylcyclopentane, cyclohexane, methylcyclohexane, and ethylcyclohexane; aromatic hydrocarbons such as benzene, toluene, chlorobenzene, and o-dichlorobenzene. The weight ratio of the polymerization solvent to the monomer is preferably in the range of 4:1 to 20:1. The polymerization yield increases in the order of o -dichlorobenzene>chlorobenzene>toluene>benzene>cyclohexane>hexane, which implies that the active complexes of the catalyst have somewhat polarity and that an increased polarity of the polymerization solvent stabilizes the complexes to increase the polymerization yield.

The polymerization solvent, which has a significant effect on the polymerization reaction, should be used under the condition free from oxygen and water. The polymerization reaction is initiated in the high-purity nitrogen atmosphere, and the polymerization temperature is preferably in the range from the ambient temperature to 100° C.

The cyclic polymer prepared by the present invention has a weight average molecular weight (M_(w)) of 20,000 to 1,500,000, and a molecular weight distribution (MWD) of 1.5 to 3.5. The polymerization reaction is carried out for 1 to 3 hours under a proper catalytic condition to produce a cyclic polymer in a yield of 70 to 100%. The reaction product after the polymerization reaction is precipitated with methanol or ethanol.

As described above, the cyclic polymer with a high molecular weight can be prepared in a high yield.

DETAILED DESCRIPTION OF THE INVENTION

Now, the present invention will be described in further detail by way of the following Examples, which are not intended to limit the scope of the present invention.

EXAMPLE 1

A catalyst for addition polymerization was prepared from nickel(2-ethylhexanoate)₂ (in 1% cyclohexane solution), methylaluminoxane (in 7% toluene solution) and boron trifluoride dibutyl etherate (in 5% toluene solution). Here, nickel(2-ethylhexanoate)₂ was used in an amount of 1.0×10⁻⁴ mole per 10 g of the monomer.

First, a sufficient amount of nitrogen was blown into a pressure reactor for polymerization. Toluene and norbornene were added to the reactor. Then, nickel(2-ethylhexanoate), methylaluminoxane and boron trifluoride dibutyl etherate were sequentially added to the reactor (the molar ratio was 1:100:10, respectively). The polymerization reaction was carried out at 40° C. for 3 hours. Here, the weight ratio of a polymerization solvent to the monomer was 4.3:1. The reaction product thus obtained was precipitated with ethanol to complete the reaction.

EXAMPLES 2 TO 16

The procedures were performed to prepare polynorbornene in the same manner as described in Example 1, excepting that the conditions such as catalyst composition, polymerization solvent, polymerization time, fluorine-containing compound and polymerization temperature were varied as presented in Table 1.

TABLE 1 Poly- Weight meriza- Ratio of tion Polymerization Molar Solvent/ Sol- Temp. Div.¹⁾ Catalyst²⁾ Ratio Monomer vent³⁾ (° C.) Example 1 Nickel(2-EHA)₂/ 1:100:10 4.3 Toluene 40 MAO/BF₃.OBu₂ Example 2 Nickel(2-EHA)₂/ 1:100:5 4.3 Toluene 40 MAO/BF₃.OBu₂ Example 3 Nickel(2-EHA)₂/ 1:100:3 4.3 Toluene 40 MAO/BF₃.OBu₂ Example 4 Nickel(2-EHA)₂/ 1:100:1 4.3 Toluene 40 MAO/BF₃.OBu₂ Example 5 Nickel(2-EHA)₂/ 1:25:10 4.3 Cl-Bz 40 MAO/ BF₃.CH₃COOH Example 6 Nickel(2-EHA)₂/ 1:25:30 4.3 Cl-Bz 40 MAO/BF₃.THF Example 7 Nickel(2-EHA)₂/ 1:25:10 4.3 Cl-Bz 40 MAO/BF₃.2H₂O Example 8 Nickel(2-EHA)₂/ 1:25:10 8.7 Cl-Bz 40 MAO/BF₃.NEtH₂ Example 9 Nickel(2-EHA)₂/ 1:25:10 4.3 Cl-Bz 40 MAO/HF.OBu₂ Example Nickel(2-EHA)₂/ 1:25:5 4.3 Cl-Bz 40 10 MAO/HF.OBu₂ Example Nickel(2-EHA)₂/ 1:25:10 4.3 Cl-Bz 40 11 MAO/ HF.pyridine Example Nickel(2-EHA)₂/ 1:20:5 8.7 o-Cl-Bz 60 12 MAO/BF₃.OBu₂ Example Nickel(2-EHA)₂/ 1:20:5 8.7 o-Cl-Bz 40 13 MAO/BF₃.OBu₂ Example Nickel(2-EHA)₂/ 1:20:5 8.7 o-Cl-Bz 20 14 MAO/BF₃.OBu₂ Example Nickel(2-EHA)₂/ 1:20:5 8.7 o-Cl-Bz  0 15 MAO/BF₃.OBu₂ Example Nickel(2-EHA)₂/ 1:8:10 8.7 o-Cl-Bz 40 16 MAO/BF₃.OBu₂ Note: ¹⁾Polymerization time: Examples 1 to 4 = 3 hours; Examples 5 to 11 = 2 hours; and Examples 12 to 16 = 1 hour. ²⁾The components of catalyst were sequentially charged as indicated; Nickel(2-EHA)₂ = Nickel(2-Ethylhexanoate)₂; MAO = Methylaluminoxane. ³⁾Cl-Bz = chlorobenzene; o-Cl-Bz = o-Dichlorobenzene.

EXAMPLES 17 TO 30

The procedures were performed for polymerization in the same manner as described in Example 1, excepting that the copolymerization reaction of norbornene and norbornene derivative was carried out under the conditions as presented in Table 2.

TABLE 2 Poly- Norbor- Weight meriza- nene Ratio of tion Polymerization Molar Deriva- Nb⁴⁾/Nb Time Div.¹⁾ Catalyst²⁾ Ratio tive³⁾ Derivative (hrs) Example Nickel(2-EHA)₂/ 1:40:10 Octyl-Nb 4:1 2 17 MAO/BF₃.OBu₂ Example Nickel(2-EHA)₂/ 1:40:10 Octyl-Nb 3:2 2 18 MAO/BF₃.OBu₂ Example Nickel(2-EHA)₂/ 1:40:10 Octyl-Nb 1:1 2 19 MAO/BF₃.OBu₂ Example Nickel(2-EHA)₂/ 1:40:10 Octyl-Nb 2:3 2 20 MAO/BF₃.OBu₂ Example Nickel(2-EHA)₂/ 1:40:5 Hexyl-Nb 4:1 1 21 MAO/BF₃.OBu₂ Example Nickel(2-EHA)₂/ 1:40:5 Hexyl-Nb 3:2 1 22 MAO/BF₃.OBu₂ Example Nickel(2-EHA)₂/ 1:40:5 Hexyl-Nb 1:1 2 23 MAO/BF₃.OBu₂ Example Nickel(2-EHA)₂/ 1:40:5 Hexyl-Nb 2:3 1 24 MAO/BF₃.OBu₂ Example Nickel(2-EHA)₂/ 1:40:5 Hexyl-Nb 1:4 1 25 MAO/BF₃.OBu₂ Example Nickel(2-EHA)₂/ 1:100:5 E-Nb 9:1 1 26 MAO/BF₃.OBu₂ Example Nickel(2-EHA)₂/ 1:100:5 E-Nb 7:3 1 27 MAO/BF₃.OBu₂ Example Nickel(2-EHA)₂/ 1:100:5 E-Nb 1:1 2 28 MAO/BF₃.OBu₂ Example Nickel(2-EHA)₂/ 1:100:5 DCPD 9:1 1 29 MAO/BF₃.OBu₂ Example Nickel(2-EHA)₂/ 1:100:5 DCPD 7:3 1 30 MAO/BF₃.OBu₂ Note: ¹⁾Polymerization conditions: Polymerization temperature = 40° C.; Polymerization solvent = o-dichlorobenzene; Weight ratio of polymerization solvent/monomer = 8.7. ²⁾The components of catalyst were sequentially charged as indicated; Nickel(2-EHA)₂= Nickel(2-Ethylhexanoate)₂; MAO = Methylaluminoxane. ³⁾Octyl-Nb = 5-Octyl-2-norbornene; Hexyl-Nb = 5-Hexyl-2-norbornene; E-Nb = 5-Ethylidene-2-norbornene; DCPD Dicyclopentadiene. ⁴⁾Nb = Norbornene.

EXAMPLES 31 TO 37

The procedures were performed for copolymerization of norbornene and 5-hexyl-2-norbornene in the same manner as described in Example 17, excepting that the conditions such as the catalyst composition and the fluorine-containing compound were varied as presented in Table 3.

TABLE 3 Weight Ratio of Molar Norbornene/ Div.¹⁾ Polymerization Catalyst²⁾ Ratio Hexyl-Nb³⁾ Example Nickel(2-EHA)₂/MAO/BF₃.OBu₂ 1:30:10 1:1 31 Example Nickel(2-EHA)₂/BF₃.NEtH₂/MAO 1:10:30 1:1 32 Example Nickel(2-EHA)₂/MAO/HF.OBu₂ 1:30:10 1:1 33 Example Nickel(2-EHA)₂/MAO/HF.pyridine 1:30:10 1:1 34 Example Nickel(2-EHA)₂/MAO/BF₃.THF 1:30:10 1:1 35 Example Nickel(2-EHA)₂/MAO/BF₃.2H₂O 1:30:10 1:1 36 Example Nickel(2-EHA)₂/MAO/ 1:30:10 1:1 37 BF₃.CH₃COOH Note: ¹⁾Polymerization conditions: Polymerization temperature 40° C.; Polymerization time = 1 hour; Weight ratio of polymerization solvent/monomer = 8.7. ²⁾The components of catalyst were sequentially charged as indicated; Nickel(2-EHA)₂ = Nickel(2-Ethylhexanoate)₂; MAO = Methylaluminoxane. ³⁾Hexyl-Nb = 5-Hexyl-2-norbornene.

COMPARATIVE EXAMPLES 1 TO 11

The procedures were performed to prepare a polynorbornene polymer in the same manner as described in Example 1, excepting that (1) the fluorine-containing compounds of the formulas 1 to 7 were not used; that (2) another metal salt compound was used as a main catalyst; that (3) another cocatalyst other than the fluorine-containing compounds of the formulas 1 to 7 was used; or that (4) an aluminum compound was used instead of MAO. The results are presented in Table 4.

TABLE 4 Poly- Weight meriza- Ratio of tion Polymerization Molar Solvent/ Sol- Time Div.¹⁾ Catalyst²⁾ Ratio Monomer vent³⁾ (hr) Compara- Nickel(2-EHA)₂/ 1:20 8.7 Cl-Bz 1 tive MAO Example 1 Compara- Co(naph)₂/ 1:200 4.3 Toluene 3 tive MAO Example 2 Compara- Co(naph)₂/ 1:200 4.3 CHX 3 tive MAO Example 3 Compara- Nickel(2-EHA)₂/ 1:100 4.3 Toluene 3 tive MAO Example 4 Compara- Nickel(2-EHA)₂/ 1:25:10 4.3 Cl-Bz 2 tive MAO/BF₃.H₃PO₄ Example 5 Compara- Nickel(2-EHA)₂/ 1:25:10 4.3 Cl-Bz 2 tive MAO/ Example 6 BF₃.S(CH₃)₂ Compara- Nickel(2-EHA)₂/ 1:100:10 4.3 Toluene 3 tive AlEt₃/BF₃.OBu₂ Example 7 Compara- Nickel(2-EHA)₂/ 1:50:10 4.3 Toluene 3 tive AlEt₃/BF₃.OBu₂ Example 8 Compara- Co(naph)₂/ 1:200:10 4.3 Toluene 3 tive MAO/B(C₆F₅)₃ Example 9 Compara- Nd(vers)₃/MAO 1:200 4.3 CHX 3 tive Example 10 Compara- Nd(vers)₃/Tiba/ 1:35:5:2 4.3 CHX 3 tive Dibal/Diac Example 11 Note: ¹⁾Polymerization temperature = 40° C. ²⁾The components of catalyst were sequentially charged as indicated; Nickel(2-EHA)₂ = Nickel(2-Ethylhexanoate)₂; MAO = Methylaluminoxane; Co(naph)₂ = Co(naphthenate)₂; Nd(vers)₃ = Nd(versatate)₃; Tiba = Al(i-Bu)₃; Dibal = AlH(i-Bu)₂; Diac = Al(i-Bu)₂Cl. ³⁾Cl-Bz = chlorobenzene; CHX = cyclohexane.

COMPARATIVE EXAMPLES 12 TO 16

The procedures were performed to prepare a polynorbornene copolymer in the same manner as described in Example 17, excepting that (1) the fluorine-containing compounds of the formulas 1 to 7 were not used; or that (2) another aluminum compound was used instead of MAO. The results are presented in Table 5.

TABLE 5 Norbor- Weight nene Ratio of Polymerization Molar Deriva- Nb⁴⁾/Nb Sol- Div.¹⁾ Catalyst²⁾ Ratio tive³⁾ Derivative vent⁵⁾ Compara- Nickel(2-EHA)₂/ 1:100:10 Hexyl- 1:1 Toluene tive AlEt₃/BF₃.OBu₂ Nb Example 12 Compara- Nickel(2-EHA)₂/ 1:50:10 Hexyl- 1:1 Toluene tive AlEt₃/BF₃.OBu₂ Nb Example 13 Compara- Nickel(2-EHA)₂/ 1:100 Octyl- 1:1 Toluene tive MAO Nb Example 14 Compara- Nickel(2-EHA)₂/ 1:100:10 Octyl- 1:1 Toluene tive AlEt₃/BF₃.OBu₂ Nb Example 15 Compara- Nickel(2-EHA)₂/ 1:100 E-Nb 1:1 o-Cl-Bz tive MAO Example 16 Note: ¹⁾Polymerization conditions: Polymerization time, Comparative examples 12 and 13 = 3 hours; Comparative examples 14 and 15 = 4 hours; Comparative example 16 = 2 hours; Polymerization temperature = 40° C.; Weight ratio of polymerization solvent/monomer = 8.7. ²⁾The components of catalyst were sequentially charged as indicated; Nickel(2-EHA)₂ = Nickel(2-Ethylhexanoate)₂; MAO = Methylaluminoxane. ³⁾Hexyl-Nb = 5-Hexyl-2-norbornene; Octyl-Nb = 5-Octyl-2-norbornene; E-Nb = 5-Ethylidene-2-norbornene. ⁴⁾Nb = Norbornene. ⁵⁾o-Cl-Bz = o-Dichlorobenzene.

EXPERIMENTAL EXAMPLE 1

The yields and M_(W)s of the homo- and co-polymers as prepared in Examples 1 to 37 and Comparative Examples 1 to 16 were measured. The results are presented in Table 6.

TABLE 6 Div. Yield (%) M_(W) MWD Example 1 90.0 191,000 2.74 Example 2 92.7 225,000 2.30 Example 3 81.3 258,000 2.08 Example 4 79.5 235,000 2.08 Example 5 72.8 501,000 2.31 Example 6 86.4 746,000 3.23 Example 7 84.7 578,000 2.32 Example 8 100 650,000 2.38 Example 9 97.0 623,000 2.31 Example 10 95.0 608,000 2.35 Example 11 89.0 626,000 2.40 Example 12 98.2 823,000 2.96 Example 13 100 744,000 2.54 Example 14 98.4 821,000 2.79 Example 15 98.9 913,000 2.48 Example 16 72.0 1,479,000 2.18 Example 17 98.0 485,000 3.08 Example 18 90.9 349,000 2.34 Example 19 84.1 237,000 2.37 Example 20 75.2 201,000 1.51 Example 21 100 570,000 2.69 Example 22 94.7 520,000 2.33 Example 23 91.5 530,000 2.04 Example 24 89.1 461,000 2.04 Example 25 79.8 421,000 1.81 Example 26 100 125,000 2.07 Example 27 86.3 31,000 2.23 Example 28 73.4 28,000 2.00 Example 29 100 184,000 1.78 Example 30 85.6 53,000 1.79 Example 31 86.7 878,000 2.46 Example 32 78.8 1,088,000 2.21 Example 33 82.0 884,000 2.23 Example 34 76.9 912,000 2.26 Example 35 85.9 866,000 2.65 Example 36 81.6 891,000 2.40 Example 37 71.0 944,000 2.90 Comparative 30.7 1,254,000 2.43 Example 1 Comparative 0.5 — — Example 2 Comparative 0 — — Example 3 Comparative 62.3 379,000 2.37 Example 4 Comparative 23.0 326,000 2.03 Example 5 Comparative 38.1 696,000 2.43 Example 6 Comparative 1.6 19,000 1.36 Example 7 Comparative 4.9 76,000 2.39 Example 8 Comparative 0.3 — — Example 9 Comparative 0.5 — — Example 10 Comparative 0 — — Example 11 Comparative 0 — — Example 12 Comparative 1.2 — — Example 13 Comparative 16.5 96,000 1.72 Example 14 Comparative 1.5 — — Example 15 Comparative 28.5 14,000 1.75 Example 16 @

-   -   As described above, the method for preparing homo- and         co-polymers according to the present invention includes mixing a         nickel salt compound, an organoaluminoxane compound and a         fluorine-containing compound selected from the compounds of the         formulas 1 to 7 to prepare a complex having a high solubility in         a non-polar solvent, and then polymerizing a cyclic olefin         compound in the presence of the complex as a catalyst in a         non-polar solvent, which method inhibits gel formation and         provides a cyclic polymer having a high molecular weight in a         high yield. 

1. In a method for preparing homo- and co-polymers by polymerizing cyclic olefin compounds with a catalyst in a non-polar solvent, the catalyst including a complex prepared by mixing a nickel salt compound, an organoaluminoxane compound, and at least one fluorine-containing compound selected from compounds represented by the following formulas 1 to 7: BF₃.OR₁R₂  Formula 1 Wherein, R₁ and R₂ are different or the same and independently include a substituent selected from a C₁–C₁₀ alkyl group, a C₁–C₁₀ cycloalkyl group, a C₁–C₁₀ allyl group, a C₁–C₁₀ aryl group, or C₁–C₁₀ arylalkyl group,

Wherein, R₃ is an alkyl group containing from 2 to 10 carbon atoms, HF.OR₄R₅  Formula 3 Wherein, R₄ and R₅ are different or the same and independently include a substituent selected from a C₁–C₁₀ alkyl group, a C₁–C₁₀ cycloalkyl group, a C₁–C₁₀ allyl group, a C₁–C₁₀ aryl group, or C₁–C₁₀ arylalkyl group,

Wherein, R₆ is an alkyl group containing from 2 to 10 carbon atoms,

wherein, R₇, R₈ and R₉ are different or the same and independently include a C₁–C₁₀ alkyl group, a C₁–C₁₀ cycloalkyl group, a C₁–C₁₀ aryl group, a C₁–C₁₀ arylalkyl group, or a hydrogen atom, BF₃ .nR₁₀  Formula 6 Wherein, R₁₀ is H₂O or CH₃COOH; and n is 1 or 2, HF.R₁₁  Formula 7 Wherein, R₁₁ is pyridine.
 2. The method as claimed in claim 1, wherein the compound represented by the formula 1 includes at least one selected from the group consisting of boron trifuloride dimethyl etherate, boron trifluoride diethyl etherate, and boron trifluoride dibutyl etherate.
 3. The method as claimed in claim 1, wherein the compound represented by the formula 2 includes boron trifluoride-tetrahydrofuran complex.
 4. The method as claimed in claim 1, wherein the compound represented by the formula 3 includes at least one selected from the group consisting of hydrogen fluoride dimethyl etherate, hydrogen fluoride diethyl etherate, and hydrogen fluoride dibutyl etherate.
 5. The method as claimed in claim 1, wherein the compound represented by the formula 4 includes hydrogen fluoride-tetrahydrofuran complex.
 6. The method as claimed in claim 1, wherein the compound represented by the formula 5 includes at least one selected from the group consisting of boron trifluoride-methylamine complex, boron trifluoride-ethylamine complex, boron trifluoride-propylamine complex, and boron trifluoride-butylamine complex.
 7. The method as claimed in claim 1, wherein the compound represented by the formula 6 includes at least one selected from boron trifuloride dihydrate, and boron trifluoride-acetic acid complex.
 8. The method as claimed in claim 1, wherein the compound represented by the formula 7 includes hydrogen fluoride-pyridine.
 9. The method as claimed in claim 1, wherein the nickel salt compound includes at least one nickel-carboxylate selected from the group consisting of nickel(hexanoate)₂, nickel(heptanoate)₂, nickel(octanoate)₂, nickel(2-ethylhexanoate)₂, nickel(naphthenate)₂, nickel(stearate)₂, and nickel(versatate)₂.
 10. The method as claimed in claim 1, wherein the nickel salt compound is used in an amount of 1.0×10⁻⁵ to 1.0×10⁻³ mole per 10 g of the cyclic compound.
 11. The method as claimed in claim 9, wherein the nickel salt compound is used in an amount of 1.0×10⁻⁵ to 1.0×10⁻³ mole per 10 g of the cyclic compound.
 12. The method as claimed in claim 1, wherein the organoaluminoxane compound includes at least one selected from the group consisting of methylaluminoxane, ethylaluminoxane, propylaluminoxane, butylaluminoxane, and isobutylaluminoxane.
 13. The method as claimed in claim 1, wherein the cyclic olefin compound includes at least one selected from norbornene, dicyclopentadiene, and compounds represented by the following formulas 8 and 9:

wherein, R₁₂ is a C₁–C₂₀ alkyl group,

wherein R₁₃ is a C₁–C₂₀ alkyl group.
 14. The method as claimed in claim 1, wherein the fluorine-containing compounds represented by the formulas 1 to 7 and the nickel salt compound are used at a molar ratio of 1:1 to 30:1.
 15. The method as claimed in claim 1, wherein the fluorine-containing compounds represented by the formulas 1 to 7 and the nickel salt compound are used at a molar ratio of 3:1 to 10:1.
 16. The method as claimed in claim 14, wherein the fluorine-containing compounds represented by the formulas 1 to 7 and the nickel salt compound are used at a molar ratio of 3:1 to 10:1.
 17. The method as claimed in claim 1, wherein the organoaluminoxane compound and the nickel salt compound are used at a molar ratio of 8:1 to 200:1.
 18. The method as claimed in claim 1, wherein the organoaluminoxane compound and the nickel salt compound are used at a molar ratio of 15:1 to 100:1.
 19. The method as claimed in claim 17, wherein the organoaluminoxane compound and the nickel salt compound are used at a molar ratio of 15:1 to 100:1.
 20. The method as claimed in claim 1, wherein the non-polar solvent includes at least one selected from aliphatic hydrocarbons such as hexane, isopentane, heptane, octane, or isooctane; cycloaliphatic hydrocarbons such as cyclopentane, methylcyclopentane, cyclohexane, methylcyclohexane, or ethylcyclohexane; and aromatic hydrocarbons such as benzene, toluene, chlorobenzene, or o-dichlorobenzene. 